White etching cracks
White etching cracks (WEC), or white structure flaking or brittle flaking, is a type of rolling contact fatigue (RCF) damage that can occur in bearing steels under certain conditions, such as hydrogen embrittlement, high stress, inadequate lubrication, and high temperature. WEC is characterised by the presence of white areas of microstructural alteration in the material, which can lead to the formation of small cracks that can grow and propagate over time, eventually leading to premature failure of the bearing.